QIU Yuxin, ZHANG Aijun, XIN Benbin, MENG Junhu, WU Youzhi. Microstructure, Mechanical Properties and Tribological Properties of Al0.2Co1.5CrNi1.5Ti0.5Mox High-Temperature Wear-Resisting High Entropy Alloy[J]. TRIBOLOGY, 2023, 43(12): 1381-1392. DOI: 10.16078/j.tribology.2022212
|
The Al0.2Co1.5CrNi1.5Ti0.5Mox (x=0 to 0.4) high entropy alloy was prepared by vacuum arc melting, and the influence of Mo element on the microstructure, mechanical properties and tribological properties of the high entropy alloy was analyzed. Moreover, the wear mechanism of the high entropy alloy was researched. The Al0.2Co1.5CrNi1.5Ti0.5 high entropy alloy consists of FCC phase and ordered AlNi3 phase. The addition of Mo caused the segregation of Cr and Mo, and promotes the formation of hard σ phase through the in-situ reaction of Cr and Mo atoms. With the increase of Mo content, the content of σ phase also increases gradually, and the addition of Mo makes the high entropy alloy produce obvious lattice distortion. The lattice distortion effect induced by the Mo with larger atomic radius and the precipitated phase strengthening effect of the hard σ phase endow the high entropy alloy with excellent mechanical and tribological properties. As the molar content of Mo increased from 0 to 0.4, the hardness of high entropy alloy was increased from 520 HV to 730 HV by 40.4%, and the yield strength increased by 32.1% from 1 060 MPa to 1 400 MPa. However, the hard σ phase is a brittle phase and cannot deform as the FCC phase with better plasticity at the same time, which leads to a significant decrease in the plasticity and toughness of high entropy alloys. The tribological performance of the high entropy alloy at RT~900 ℃ is characterized by ball-on-disc high temperature tribometer. The addition of Mo elements significantly improved the tribological performance of the high entropy alloy, especially when the Mo content was 0.4 mol, the wear rate at RT and 800 ℃ was 2.62×10−6 mm3/(N·m) and 6.23×10−7 mm3/(N·m), respectively, which improved by 83.4% and 89.7% compared with that of high entropy alloy without Mo. And the wear resistance is better than Inconel 718 and Stellite 6 alloys. The improvement of wear resistance was attributed to the increased micro-hardness and yield strength of the high entropy alloy at room temperature, and the wear mechanism is abrasive wear and delamination wear. The formation of the glaze layer and good high temperature softening resistance play a key role in the improvement of high temperature friction. A smooth and dense oxidized glaze layer was formed on the worn surface at high temperature, which has obvious anti-wear effects. The thickness of the glaze layer was 2 μm at 800 °C, and the thickness of the glaze layer increased to 5 μm at 900 °C. The glaze layer enhances the high temperature wear resistance of high entropy alloys, and reduces the high temperature friction coefficient. The wear mechanism changes from oxidative wear to adhesive wear. At medium temperature, the hardness of the high entropy alloy decreases to a certain extent. Moreover, the glaze layer formed on the wear surface is incomplete. Under the combined influence of the two, the wear of the high entropy alloy is aggravated and the wear resistance is reduced.
| [1] |
魏耀光, 郭刚, 李静, 等. 难熔高熵合金在航空发动机上的应用[J]. 航空材料学报, 2019, 39(5): 82–93
Wei Yaoguang, Guo Gang, Li Jing, et al. Application of refractory high entropy alloys on aero-engines[J]. Journal of Aeronautical Materials, 2019, 39(5): 82–93
|
| [2] |
Lu Chenyang, Niu Liangliang, Chen Nanjun, et al. Enhancing radiation tolerance by controlling defect mobility and migration pathways in multicomponent single-phase alloys[J]. Nature Communications, 2016, 7: 13564. doi: 10.1038/ncomms13564
|
| [3] |
Yeh J W, Chen S K, Lin S J, et al. Nanostructured high-entropy alloys with multiple principal elements: novel alloy design concepts and outcomes[J]. Advanced Engineering Materials, 2004, 6(5): 299–303. doi: 10.1002/adem.200300567
|
| [4] |
蒲科锦, 王廷军, 孟东, 等. 多主元高熵合金材料的研究进展[J]. 新技术新工艺, 2022, 410(2): 10–14
Pu Kejin, Wang Tingjun, Meng Dong, et al. Research progress of high-entropy alloys materials with multi-principal element[J]. New Technology & New Process, 2022, 410(2): 10–14
|
| [5] |
Miracle D B, Senkov O N. A critical review of high entropy alloys and related concepts[J]. Acta Materialia, 2017, 122: 448–511. doi: 10.1016/j.actamat.2016.08.081
|
| [6] |
Chuang Minghao, Tsai M H, Wang W R, et al. Microstructure and wear behavior of Al x Co1.5CrFeNi1.5Ti y high-entropy alloys[J]. Acta Materialia, 2011, 59(16): 6308–6317. doi: 10.1016/j.actamat.2011.06.041
|
| [7] |
Chang Y J, Yeh A C. The evolution of microstructures and high temperature properties of Al x Co1.5CrFeNi1.5Ti y high entropy alloys[J]. Journal of Alloys and Compounds, 2015, 653: 379–385. doi: 10.1016/j.jallcom.2015.09.042
|
| [8] |
Larissa M G, Igor M, Milan O, et al. High-strength Al0.2Co1.5CrFeNi1.5Ti high-entropy alloy produced by powder metallurgy and casting: a comparison of microstructures, mechanical and tribological properties[J]. Materials Characterization, 2020, 159: 110046. doi: 10.1016/j.matchar.2019.110046
|
| [9] |
姚小飞, 魏敬鹏, 吕煜坤, 等. (CoCrFeMnNi)97.02Mo2.98高熵合金σ相析出演变及力学性能[J]. 金属学报, 2020, 56(5): 769–775
Yao Xiaofei, Wei Jingpeng, Lv Yukun, et al. Precipitation σ phase evoluation and mechanical properties of (CoCrFeMnNi)97.02Mo2.98 high entropy alloy[J]. Acta Metallurgica Sinica, 2020, 56(5): 769–775
|
| [10] |
杜宇航, 丁德渝, 郭宁, 等. 高熵合金功能特性研究进展[J]. 材料导报, 2021, 35(17): 17051–17063
Du Yuhang, Ding Deyu, Guo Ning, et al. The progress of high-entropy alloys with the functional properties[J]. Materials Reports, 2021, 35(17): 17051–17063
|
| [11] |
王府伯. 耐磨高熵合金的制备及其性能研究[D]. 兰州: 兰州交通大学, 2021
Wang Fubo. Preparation and properties of wear-resistant high entropy alloy[D]. Lanzhou: Lanzhou Jiatong University, 2021
|
| [12] |
王昕阳, 黄燕滨, 刘谦, 等. 钼含量对碳钢表面CoCrFeNiMo高熵合金激光熔覆涂层组织结构与耐磨性能的影响[J]. 电镀与涂饰, 2020, 39(17): 1201–1208
Wang Xinyang, Huang Yanbin, Liu Qian, et al. Effect of molybdenum content on microstructure and wear resistance of laser-clad CoCrFeNiMo high-entropy alloy on carbon steel[J]. Electroplating & Finishing, 2020, 39(17): 1201–1208
|
| [13] |
Takeuchi A, Inoue A. Classification of bulk metallic glasses by atomic size difference, heat of mixing and period of constituent elements and its application to characterization of the main alloying element[J]. Materials Transactions, 2005, 46(12): 2817–2829. doi: 10.2320/matertrans.46.2817
|
| [14] |
高妞, 刘鑫旺, 吴伟峰, 等. 耐热高熵多主元合金及其强韧化研究现状[J]. 材料导报, 2021, 35(17): 17037–17042
Gao Niu, Liu Xinwang, Wu Weifeng, et al. Advances of the strengthening and toughening of high-entropy multi-principal-element heat-resistant alloys[J]. Materials Reports, 2021, 35(17): 17037–17042
|
| [15] |
王悦. Cr合金化对纳米晶(Mo xCr1− x)5Si3涂层抗氧化与耐磨损性能影响的研究[D]. 南京: 南京航空航天大学, 2010
Wang Yue. Effect of Cr alloying on oxidation resistance and wear resistance of nanocrystalline (MoxCr1−x)5Si3 films[D]. Nanjing: Nanjing University of Aeronautics and Astronautics, 2010
|
| [16] |
文成, 莫湾湾, 田玉琬, 等. 高熵合金固溶强化问题的研究进展[J]. 材料导报, 2021, 35(17): 17081–17089
Wen Cheng, Mo Wanwan, Tian Yuwan, et al. Research progress on solid solution strengthening of high entropy alloys[J]. Materials Reports, 2021, 35(17): 17081–17089
|
| [17] |
Joele M, Matizamhuka W R. A review on the high temperature strengthening mechanisms of high entropy superalloys (HESA)[J]. Materials, 2021, 14(19): 5835. doi: 10.3390/ma14195835
|
| [18] |
Carneiro Í, Simões S. Strengthening mechanisms in carbon nanotubes reinforced metal matrix composites: a review[J]. Metals, 2021, 11(10): 1613. doi: 10.3390/met11101613
|
| [19] |
Greer J R, De Hosson J T M. Plasticity in small-sized metallic systems: intrinsic versus extrinsic size effect[J]. Progress in Materials Science, 2011, 56(6): 654–724. doi: 10.1016/j.pmatsci.2011.01.005
|
| [20] |
Xin Benbin, Zhang Aijun, Han Jiesheng, et al. The tribological properties of carbon doped Al0.2Co1.5CrFeNi1.5Ti0.5 high entropy alloys[J]. Wear, 2021, 484–485: 204045.
|
| [21] |
Xin Benbin, Zhang Aijun, Han Jiesheng, et al. Improving mechanical properties and tribological performance of Al0.2Co1.5CrFeNi1.5Ti0.5 high entropy alloys via doping Si[J]. Journal of Alloys and Compounds, 2021, 869: 159122. doi: 10.1016/j.jallcom.2021.159122
|
| [22] |
王东胜, 王士月, 孙士斌, 等. 一种船用低温钢板在干态室温下的往复摩擦特性研究[J]. 表面技术, 2017, 46(8): 120–127
Wang Dongsheng, Wang Shiyue, Sun Shibin, et al. Study on reciprocating friction characteristics of a marine low temperature steel plate at dry room temperature[J]. Surface Technology, 2017, 46(8): 120–127
|
| [23] |
柏伟, 张爱军, 孟军虎, 等. (CuMnNi)100-xAlx高熵铜合金的显微组织、力学与摩擦学性能研究[J]. 摩擦学学报, 2021, 41(5): 609–618 doi: 10.16078/j.tribology.2020180
Bai Wei, Zhang Aijun, Meng Junhu, et al. Microstructure, mechanical and tribological properties of (CuMnNi)100-xAlx High Entropy Bronzes[J]. Tribology, 2021, 41(5): 609–618 doi: 10.16078/j.tribology.2020180
|
| [24] |
王奕迪, 李晓倩, 陈端杰, 等. 近单一FCC相AlCoCrFeNi高熵合金的常温摩擦学行为及典型磨损机制[J]. 摩擦学学报, 2023, 43(2): 197–208 doi: 10.16078/j.tribology.2021266
Wang Yidi, Li Xiaoqian, Chen Duanjie, et al. Tribological behaviors and typical wear mechanisms of nearly single FCC phase AlCoCrFeNi high-entropy alloy at ambient temperature[J]. Tribology, 2023, 43(2): 197–208 doi: 10.16078/j.tribology.2021266
|
| [25] |
Ye Y X, Liu C Z, Wang H, et al. Friction and wear behavior of a single-phase equiatomic TiZrHfNb high-entropy alloy studied using a nanoscratch technique[J]. Acta Materialia, 2018, 147: 78–89. doi: 10.1016/j.actamat.2018.01.014
|
| [26] |
马文林, 王府伯, 张爱军, 等. CoCrFeMoNiCx中熵合金的组织及其力学和摩擦学性能[J]. 摩擦学学报, 2021, 41(6): 913–923. doi: 10.16078/j.tribology.2020267
Ma Wenlin, Wang Fubo, Zhang Aijun, et al. Microstructure, mechanical and tribological properties of CoCrFeMoNiCx medium entropy alloys[J]. Tribology, 2021, 41(6): 913–923 doi: 10.16078/j.tribology.2020267
|
| [27] |
张爱军, 韩杰胜, 苏博, 等. AlCoCrFeNi高熵合金的高温摩擦磨损性能[J]. 摩擦学学报, 2017, 37(6): 776–783 doi: 10.16078/j.tribology.2017.06.008
Zhang Aijun, Han Jiesheng, Su Bo, et al. Tribological properties of AlCoCrFeNi high entropy alloy at elevated temperature[J]. Tribology, 2017, 37(6): 776–783 doi: 10.16078/j.tribology.2017.06.008
|
| [28] |
梁源, 邢怀中, 晁明举, 等. CO2激光烧结合成负热膨胀材料Sc2(MO4)3(M=W, Mo)及其拉曼光谱[J]. 物理学报, 2014, 63(24): 248106 doi: 10.7498/aps.63.248106
Liang Yuan, Xing Huaizhong, Chao Mingju, et al. Syntheses of negative thermal expansion materials Sc2(MO4)3 (M =W, Mo) with a CO2 laser and their Raman sp ectra[J]. Acta Physica Sinica, 2014, 63(24): 248106 doi: 10.7498/aps.63.248106
|
| [29] |
Xin Benbin, Zhang Aijun, Han Jiesheng, et al. Tuning composition and microstructure by doping Ti and C for enhancing mechanical property and wear resistance of Al0.2Co1.5CrFeNi1.5Ti0.5 high entropy alloy matrix composites[J]. Journal of Alloys and Compounds, 2020, 836: 155273. doi: 10.1016/j.jallcom.2020.155273
|
| [30] |
彭玉春, 陈泷, 张祥雷, 等. 高温滑动摩擦中釉质层的综述研究[J]. 材料保护, 2022, 55(6): 147–153
Peng Yuchun, Chen Long, Zhang Xianglei, et al. A review on glaze layers in high temperature sliding friction[J]. Materials Protection, 2022, 55(6): 147–153
|
Supported by: Beijing Renhe Information Technology Co., Ltd. 
DownLoad: