常用实木地板的摩擦磨损性能研究

刘振东; 王文波; 蔡雷; 郭东杰; 戴振东

常用实木地板的摩擦磨损性能研究

刘振东^1,2,
王文波³,
蔡雷^1,2,
郭东杰³,
戴振东^3, ,

1.
1. 南京航空航天大学机电学院,南京 210016
2.
2. 南京航空航天大学高新技术研究院仿生结构与材料防护研究所,南京 210016
3.
南京航空航天大学高新技术研究院仿生结构与材料防护研究所,南京 210016

基金项目:

自然科学基金重大国际合作项目(60910007)和固体润滑国家重点实验室开放基金资助.

详细信息

中图分类号: TH117.3
计量
- 文章访问数: 2246
- HTML全文浏览量: 16
- PDF下载量: 2010
出版历程
- 收稿日期: 2012-06-26
- 修回日期: 2012-07-05

Friction and Wear Properties of Commercial Solid Wood Floorings

1.
1. College of Mechanical and Electrical Engineering,Nanjing University of Aeronautics and Astronautics, Nanjing 210016,China
2.
2. Institute of Bioinspired Structure and Surface Engineering,Nanjing University of Aeronautics and Astronautics, Nanjing 210016,China
3.
Institute of Bioinspired Structure and Surface Engineering,Nanjing University of Aeronautics and Astronautics, Nanjing 210016,China

摘要

摘要: 用UMT-2MT摩擦试验机测试了9种常用实木地板对橡胶和440C不锈钢的摩擦磨损性能.结果表明:橡胶对多数地板的摩擦系数大于0.5,满足安全标准,且均大于钢球对地板的摩擦系数.钢球对地板漆层的摩擦系数介于0.1~0.6之间,而钢球对地板木材的摩擦系数基本相同,处于0.55左右.橡胶对地板磨损试验未能得到可测的磨损量(试验时间为1 h).钢球对地板漆层和木材层的磨损不同,漆层的抗磨损能力普遍高于木质层.每种地板都有临界载荷,载荷小于临界载荷时,随着载荷的增加磨损量几乎不变;载荷大于临界载荷后,随着载荷的增加磨损明显加快.
- 实木地板 /
- 漆层 /
- 耐磨性 /
- 磨损量
Abstract: The friction and wear properties of nine kinds of typical solid wood floorings were investigated using the tribometer of UMT-2MT. The coefficients of friction (COFs) between rubber shoe sole and floor were much higher than that between stainless steel ball and floor. For the nine different solid wood floorings, the COFs between stainless steel ball and lacquer for floor varied significantly from 0.1 to 0.6, while the COFs between stainless steel and solid wood of floors were nearly a constant around 0.55. The wear of floors was un-detectable when rubber shoe sole was experimented with floor for one hour. As stainless steel ball rubbed on the floorings, the anti-wear properties of lacquer for floors were better than that of solid wood. And a critical loading for each floorings was set up. As loads were lower than the critical one, the wear of floors was negligible, while higher than the critical load, the wear was much higher and increased quickly with increasing load. The experiments raise a possibility to evaluate the anti-wear properties of lacquer for floor and how to protect the floors from early wear by using right shoes.
- solid wood flooring /
- lacquer layer /
- resistance to wear /
- wear

HTML全文

参考文献(15)

[1]	高为,武广明,付正.三层实木复合地板性能特点及工艺关键[J].木业科技,2001, 26(3):40-42. Gao W, Wu G M, Fu Z. Characteristic of three-layer fished parquet floor and the key manufacture technology[J].Forestry Science&Technology,2001,26(3):40-42.
[3]	陈国本.浅议我国研究和制定地面防滑标准的迫切性[J].石材,2008,(01):33-36. Chen G B. A preliminary study of the urgency of research and formulation of floor slip-resistance standards in China[J].Stone,2008,(01):33-36.
[4]	Beschorner K E,Redfern M S,Porter W L,et al.Effects of slip testing parameters on measured coefficient of friction[J].Applied Ergonomics,2007,38(6):773-780.
[5]	Ali W Y. Friction coefficient of bare foot sliding against marble flooring tiles[J]. Journal of King Abdulaziz University,2010,21(1):57-72.
[6]	王柏生,张向辉.高校既有建筑地面抗滑性能试验研究[J].摩擦学学报,2011,31(2):187-193. Wang B S, Zhang X H. The experimental study of slip-resistance of existing floors on a college campus[J].Tribology, 2011, 31(2):187-193.
[7]	中华人民共和国国家标准.实木地板(GB/T 15076)[S].北京:中国标准化出版社, 2009. China National Standards.Solid wood flooring(GB/T 15076)[S].Beijing:China standardization press,2009.
[8]	BS EN 13696, Wood flooring -test methods to determine elasticity and resistance to wear and impact resistance[S]. European Standard.
[9]	DIN 18032-1-2003.Halls and rooms for sports and multi-purpose use-Part 1:Planning principles(S). Deutsche Norm.
[10]	周晓虹,徐淑华,邢航. 关于集成材,地板块生产工艺及设备配置的探讨[J].木材加工机械,2002,13(4):23-24. Zhou X H, Xu S H, Xing H. Discussion on production technology discussion on production technology and equipment distribution of laminated finger- joint board and flooring board[J]. Wood Processing Machinery, 2002, 13(4):23-24.
[11]	石雷,刘维民. Cu/Ni-P多层膜的制备及其摩擦学性能研究[J].摩擦学学报, 2004, 24(5):397-401. Shi L,Liu W M.Preparation and tribological properties of Cu/Ni-P multilayer electrodeposited on beryllium bronze[J].Tribology,2004,24(5):396-401.
[12]	濮春欢,徐滨士,王海斗,等. 不同载荷下3Cr13不锈钢涂层磨损寿命研究[J].摩擦学学报,2010,30(1):75-79. Pu C H,Xu B S,Wang H D,et al.Wear lifetime of 3Cr13 stainless steel coating under various loads[J].Tribology,2010,30(1):75-79.
[13]	王卫东, 钟家林, 卢晓宁. 抗菌耐磨实木复合地板的性能分析[J]. 木材工业, 2004, 18(6):36-37. Wang W D, Zhong J L, Lu X N. A new type of parquet with resistance to fungus and abrasion[J].China Wood Industry, 2004, 18(6):36-37.
[14]	董育华,马克骏,吕斌,等. CK-2耐磨树脂提高实木地板表面耐磨性[J].木材工业,2000,14(3):33-34. Dong Y H, Ma K J, Lu B. CK-2 Abrasion-proof resin for improving surface wear-resistance of solid wood flooring[J].China Wood Industry,2000,14(3):33-34.
[15]	赵兴中,刘家浚,朱宝亮.干摩擦及水或油润滑下TiC(N)-Al₂O₃陶瓷/不锈钢摩擦副的磨损性能研究[J].摩擦学学报,1998,18(1):7-12. Zhao X Z, Liu J J, Zhu B L.Wear properties of TiC(N) -Al₂O₃ composite ceramic-stainless steel pair under dry and lubricated conditions[J].Tribology,1998,18(1):7-12.
[16]	葛世荣王伟华,王军祥.玻璃纤维增强尼龙1010复合材料的摩擦学性能研究[J].摩擦学学报, 2000, 20(6):427-430. Ge S R,Wang W H,Wang J X.Investigation of the tribological properties of glass fiber reinforced polyamide-1010 composite[J].Tribology,2000,20(6):427-430.